UkuSila iSteel Shot
Imodeli/ubungakanani:0.4-2.5mm
Iinkcukacha zeMveliso:
Ingxubevange yokudubula intsimbi yokusila isekelwe kukudubula kwentsimbi yekhabhoni ephezulu, ukudutyulwa kwentsimbi ephantsi kwekhabhoni, kunye nokudubula kwentsimbi ephantsi ye-vanadium, kuthathelwa ingqalelo ubuthathaka obubulalayo bezi mveliso zingasentla: umngxuma womoya, iintanda, umahluko wobulukhuni, phuhlisa iimveliso ezintsha ngokuphinda zisetyenziswe. itekhnoloji yokubumba, inokukhetha izinto ezahlukeneyo ngokusetyenziswa okwahlukileyo, iindleko zayo zixhomekeke kwindawo yesicelo, inobude bokusebenzisa ubomi, inexabiso eliphezulu ukusebenza.steel cut wire shots zifumaneka kubulukhuni obuthathu obahlukeneyo: 45-50 HRC , 50-55 HRC kunye ne-55-60 HRC kunye nobukhulu obuvela kwi-0.20mm ukuya kwi-2.50mm.Ukudubula kwethu ngocingo okusikiweyo kuhambelana ne-SAE J441, AMS 2431 kunye ne-VDFI 8001.
IiNgcaciso eziphambili:
| SIZE: | 0.2-2.5MM |
| UBUNZIMA: | HRC40-50 HRC45-55 HRC50-60 HRC>60 |
| ISHAPE | G1 inemiqathango G2 ikwimeko ephindwe kabini I-G3 eSpherical |
| IPROJEKTHI | INGCACISO | INDLELA YOVAVANYO | |||
| UHLELO LWEKHEMICAL | C | 0.45-0.75% | P | ＜0.04% | ISO 9556:1989 ISO 439:1982 ISO 629:1982 ISO 10714:1992 |
|
| Si | 0.10-0.30% | Cr | / |
|
|
| Mn | 0.40-1.5% | Mo | / |
|
|
| S | ＜0.04% | Ni | / |
|
| IMICROTRUCTURE | Martensite okanye troosite okanye pearlite deformed | GB/T 19816.5-2005 | |||
| Ukuxinana | ≥7.40g/cm³ | GB/T 19816.4-2005 | |||
| NGAPHANDLE | Ubungakanani obufanayo, ukumenyezela okugqibeleleyo, ukumila kwebhola | Okubonakalayo | |||
Kutheni ukhetha iAlloy Grinding Shot?
Ukusila icandelo lomnqamlezo wokudubula
Steel shot cross icandelo
Ukugaya Shot Materials ekrwada
Steel Shot Raw Materials
①, Yenziwe ngocingo lwentsimbi ebunjiweyo, akukho mngxuma womoya, iintanda, kunye nokwahluka kobulukhuni.
②, Ngokweemfuno ezahlukeneyo zemimandla eyahlukeneyo, sinokukhetha izixhobo ezahlukeneyo zocingo lwentsimbi.
③,Isithonga sokuSila sinokomelela ngakumbi, kwaye ubomi buphinda-phindwe ka-1.5 bokudubula kwentsimbi.
④，Isixhobo sokusebenza esicocwe ngokuSila isithonga simhlophe-yisilivere, kwaye umphezulu ococwe ngentsimbi yeCast shot uba mnyama.
⑤，Isiphumo sokucoca sicokisekile ngakumbi kunokudubula kwentsimbi, kwaye akukho mfuneko yokucoca okwesibini.Emva kokucoca, uburhabaxa be-workpiece buhlangabezana neemfuno.
⑥, Ngenxa yeenzuzo zokungabikho komngxuma womoya, akukho zintanda, kwaye akukho lula ukwaphulwa kwi-abrasive forging forging steel shot, isixa sokuzalisa kwinkqubo yokuqhushumba sincinci, uthuli kwinkqubo yokuqhushumba luncinci, amandla okusebenza aphantsi. , kunye nongcoliseko lokusingqongileyo kunokuncipha.
Ukuthelekiswa kweengenelo
|
| Ukudubula kwentsimbi yekhabhoni ephantsi | Ukudubula kwentsimbi yokusila | High carbon steel shot |
| C | 0.08-0.20 | 0.45-0.75 | 0.80-1.20 |
| S | ≤0.05 | ＜0.03 | ≤0.05 |
| Mn | 0.35-1.50 | 0.50-1.50 | 0.50-1.20 |
| P | ≤0.05 | ＜0.03 | ≤0.05 |
| Si | 0.10-2.00 | 0.30-0.60 | ≥0.40 |
| HRC | 40-50 | 40-60/50-60 | 40-50 |
| Ubutyuwa | ≤45mg/㎡ | ≤18mg/㎡ | ≤45mg/㎡ |
| ubomi bokudinwa | 4000-4200 | 5400-5800 | 2500-2800 |