Grit ya chuma ya Angular ya chini ya Carbon
Maelezo Muhimu:
| PROJECT | MAALUM | NJIA YA MTIHANI | |||
| UTUNGAJI WA KEMIKALI | C | 0.08-0.2% | P | ≤0.05% | ISO 9556:1989 ISO 439:1982 ISO 629:1982 ISO 10714:1992 |
|
| Si | 0.1-2.0% | Cr | / |
|
|
| Mn | 0.35-1.5% | Mo | / |
|
|
| S | ≤0.05% | Ni | / |
|
| MICROTRUCTURE | Homogeneous Martensite au Bainite | GB/T 19816.5-2005 | |||
| Msongamano | ≥7.0-10³kg/m³ (7.0kg/dm³) | GB/T 19816.4-2005 | |||
| MAMBO YA NJE | Wasifu wa uso uliowekwa au wa angular, Shimo la hewa <10%. | Visual | |||
| UGUMU | HV:390-530(HRC39.8-51.1) | GB/T 19816.3-2005 | |||
Hatua za Uchakataji:
Chakavu→Chagua&Kukata→Kuyeyusha→Kusafisha→Kuondoa kaboni
GHARAMA CHINI YA AIDHA YA CHUMA CHA KABANI
• Utendaji zaidi ya 20% dhidi ya risasi za juu za kaboni
• Kupungua kwa mitambo na vifaa kutokana na ufyonzwaji mkubwa wa nishati katika athari kwenye vipande.
• Chembe zisizo na kasoro zinazotokana na matibabu ya joto, fractures au nyufa ndogo
KUBORESHA MAZINGIRA
• Kupunguza unga
• Muundo mdogo wa Bainitic huhakikisha kwamba hazitavunjika wakati wa maisha yake muhimu
MUONEKANO WA JUMLA
Sura ya risasi ya chuma cha chini ya kaboni ni sawa na spherical.Uwepo mdogo wa chembe ndogo, zilizoharibika na pores, slag au uchafu inawezekana.
Hii haiathiri utendaji wa risasi, inaweza kuthibitishwa kwa kupima utendaji wake kwenye mashine.
UGUMU
Muundo wa bainitic huhakikisha kiwango cha juu cha ugumu.90% ya chembe ni kati ya 40 - 50 Rockwell C.
Kaboni ya chini katika usawa na manganese inathibitisha maisha ya muda mrefu muhimu ya chembe, hivyo kuboresha usafi wa vipande, kwa kuwa kwa kazi ya mitambo huongeza ugumu wao.
Nishati ya mlipuko wa risasi inafyonzwa hasa na sehemu, hivyo kupunguza kuvaa kwa mashine.
KUCHUKUA CARBON, UTENDAJI WA JUU
Utumiaji wa risasi ya chuma ya kaboni ya chini ina wigo wa mashine zilizo na turbine za 2500 hadi 3000 RPM na kasi ya 80 M / S.
Kwa vifaa vipya vinavyotumia 3600 RPM turbines na kasi ya 110 M / S, haya ni mahitaji ya kuongeza tija.