High Carbon Angular Steel Grit
Fa'ata'ita'iga/Lapopoa:G12-G150 Φ0.1mm-2.8mm
Fa'amatalaga o oloa:
High carbon angular u'amea u'amea e gaosia mai le maualuga carbon u'amea fana.u'amea u'amea e nutimomoia i foliga ma'a mafolafola ma mulimuli ane fa'afefe i ni ma'a'a eseese se tolu (GH, GL ma le GP) e fa'amalieina mo fa'aoga eseese.O le u'amea u'amea maualuga e masani ona fa'aogaina e fai ma ala fa'asalalau mo le fa'a'ele'ele o vaega u'amea a'o le'i fa'apipi'iina.
Fa'amatalaga autu:
| GALUEGA | FAAMATALAGA | METOGA FA'SU'EGA | |||
| FA'AIGA KEMIMI |
| 0.8-1.2% | P | ≤0.05% | ISO 9556:1989 ISO 439:1982 ISO 629:1982 ISO 10714:1992 |
| Si | ≥0.4% | Cr | / | ||
| Mn | 0.35-1.2% | Mo | / | ||
| S | ≤0.05% | Ni | / | ||
| FA'ATA'IGA | Faʻatasi Martensite poʻo Bainite | GB/T 19816.5-2005 | |||
| Malosi | ≥7.0-10³kg/m³（7.0kg/dm³） | GB/T 19816.4-2005 | |||
| FAAMATALAGA IFO | Fa'ailoga mata'itusi po'o le fa'ama'i fa'ata'oto, Pu ea <10%. | Vaaiga | |||
| MAAGA | HV:390-720(HRC39.8-64) | GB/T 19816.3-2005 | |||
Fa'agaioiina Laasaga:
Talosaga:
High Carbon Steel Grit GP:E sili ona maualalo le maaa i le va o le 40 i le 50 HRC ma e fa'aaloalogia foi e pei o le angular shot, aua o le grit o le a maua se foliga lapotopoto i lona olaga atoa.E masani ona faʻaaogaina i masini faʻafefe uili ma e lelei iʻuga i le fale gaosi oloa aua e faʻamama vave ma sina faʻaopoopoga o tau o le tausiga ma le ofuina o vaega o masini.E fa'aaogaina le GP mo le fa'amamā, fa'amama ma fa'amama.
GL:E feololo le maaa ile va ole 50 i le 60 HRC.E fa'aaogaina i masini pa'u uili ma potu fa'atosina ma e fa'apitoa i le fa'amama mamafa ma le tapenaina o mea mana'omia.E ui o le GL e feololo le ma'a'a, e leiloa fo'i lona foliga fa'ata'ita'i a'o fa'apa fana.
High Carbon Steel Grit GH: Le maualuga maaa e amata mai i le 60 i le 64 HRC.E tumau fa'aituau i le fa'afefiloi fa'agaioiga ma o lea e fetaui lelei mo mana'oga etching luga.E masani ona fa'aogaina le GH i totonu o potu fa'afefe (mea fa'apipi'i fa'apipi'i le ea.) mo le fa'amama vave ma maua ai se fa'ailoga taula a'o le'i fa'apipi'iina.